Polycrystalline mat 1600 ° C

TEMPERATURE RESISTANCE

1600 ° C KFT

MATERIAL

Polycrystalline

PRODUCT TYPE

Mat (blanket)
Clear
SKU: N/A Category:
Z

Temperature resistance

High temperature resistance up to 1600 ° C.

Z

tensile strenght

High tensile strength and resilience.

Z

Thermal conductivity

Low thermal conductivity.

PROPERTIES

Our polycrystalline mat 1600 ° C is a light, flexible mat, needled with polypropylene threads, made from high-purity polycrystalline wool. The polypropylene threads allow a higher strength and flexibility of the mat. The temperature resistance is up to 1600 ° C. Our polycrystalline mat 1600 ° C can be used in a variety of applications. It is particularly suitable for applications where shot (melt beads) are not desired or where resistance to corrosion is important.

advantages

  • High temperature resistance (up to 1600 ° C)
  • Low thermal conductivity
  • no visible shot
  • Thermal shock resistance & durability
       to chemicals
  • High tensile strength and resilience
  • insoluble in water
  • suitable for facings and anchor modules

PRODUCT TYPE

Mats (blankets) made of high temperature wool are needled lightweight mats made of ceramic (ASW / RCF) or biosoluble (AES) high temperature wool (HTW) and represent an effective solution for a wide range of thermal insulation applications. They are characterized by excellent insulating properties, high resistance to chemicals, elasticity and dimensional stability. They are exclusively inorganic and therefore no smoke or vapors are generated when exposed to heat. They are available in a wide range of densities and thickness combinations, making them one of the most versatile product groups on the market.

MATERIAL

Polycrystalline wool (PCW Poly Crystalline Wool) consist of fibers with a very high alumina content (Al2O3 > 70% by weight %). They are produced from aqueous spinning solutions using the “sol-gel process”. During the subsequent heat treatment, the previously produced, water-soluble green fibers crystallize. Polycrystalline wools are generally used at operating temperatures> 1300 ° C or, in the case of critical chemical and physical application conditions, also at lower temperatures. The first production of polycrystalline wool can be traced back to the 1970s.

Product variations

$

Roll goods

Fiber mats are sold as roll goods as standard. The roll length depends on the selected thickness. As a standard width, we have 610mm wide rolls from stock. Double widths are available on request.

KS_Packungen_Schnuere_Baender_Schlaeuche
$

Molded parts

We manufacture molded parts according to your specifications. The roll goods are made using

  • Water jet
  • Punching
  • Plotting

brought into the right shape for you.

KS_Fasermodule
$

Fiber modules

We manufacture fiberModules which are designed for the insulation requirements of industrial furnaces, kilns and heaters.

TECHNICAL DETAILS

Chemical Analysis 
Al2O3: 95,0 – 97,0
SiO2: 3,0 – 5,0
Other: <0.5

 

Physical Properties
Colour: White
Classification temperature (° C): 1600
Specific heat at 1000 ° C (J / KgK) 1000
Density (kg / m3) 96
Mean fiber diameter (μm) 3 – 4

 

Permanent linear shrinkage (%) after 24 hours
1500 ° C: <4